Er5356 Shipbuilding Welding Wire
Common shipbuilding welding wires include straight wire, coiled wire, barrel wire, etc. The specifications range from 1.0mm to 6.0mm, and can also be customized according to customer needs.
GMT- 1100, 1050, 1070, 1080 pure aluminum welding wire is suitable for MIG and TIG welding. This kind of welding wire has good color matching after anodization. With good corrosion resistance and excellent electrical conductivity. It is used for power applications of ships.
The aluminum silicon wire is insensitive to hot cracking and used for welding forged and cast materials. It is applicable for ships, motorcycles, chemicals, food, sports equipment, molds, furniture, containers, containers, etc.
GMT-5356, 5183, 5554, 5556 aluminum-magnesium alloy welding wire is specially designed for welding 5 series alloys and filler alloys whose chemical composition is close to the base metal. It has good corrosion resistance and color matching after anodization.
ER1100 is a filler metal with an aluminum content of 99%, which can be used in construction, decoration and equipment, metallurgy, pipelines, spinning equipment and other industries. It is generally used for the welding of 1100 and 3003 aluminum alloy. The welding wire is slightly golden yellow after anodization treatment, and the tensile strength of the weld is 110MP.
It is a pure aluminum welding wire with an aluminum content of more than 99.5%. It has good weldability and corrosion resistance, as well as excellent plasticity and toughness, but low strength, which is suitable for argon arc welding and oxygen-acetylene gas welding of pure aluminum and aluminum alloys with low joint requirements.
ER4043 is an aluminum brazing filler metal containing 5% silicon that can be used to weld 3003, 3004, 5052, 6061, 6063 and cast metals 355, 356 and 214. The color after anodization is off-white, and the minimum tensile strength is 186MP.
It is often used as a filling material for argon arc welding and oxygen-acetylene gas welding of aluminum alloy workpieces and castings other than aluminum-magnesium alloys, especially aluminum alloys that are prone to hot cracks after heat treatment to achieve better results.
ER5183 is usually used as ALMg4.5Mn alloy solder with a magnesium content of 4.3-5.0%, a manganese content of 0.5-1.0%, and appropriate chromium and titanium content. It is applicable for the welding of 5083, 5086, 5456, 5052, 5652 and 5056. The color of ER5183 is white after anodization, and the tensile strength of the weld is 294MP.
ER5356 tig rod is commonly used as ALMg5, which is an aluminum alloy filler metal containing up to 5% magnesium. It can be used for MIG or TIG welding. The welds of 5454 and 5456 are white anodized and have a tensile strength of 290MP. It is for welding or surface surfacing of cast and forged aluminum alloys containing 5% magnesium.